EN 10216-2 Kemisk sammansättning
|
Stålkvalitet |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
Alparvel |
Cu |
Ti max |
|
|
Namn på stål |
Stålnummer |
max |
max |
|||||||||
|
P195GH |
1.0348 |
=0.13 |
=0.35 |
=0.70 |
0.025 |
0.020 |
=0.30 |
=0.08 |
=0.30 |
=0.020 |
=0.30 |
0.040 |
|
P235GH |
1.0345 |
=0.16 |
=0.35 |
=1.20 |
0.025 |
0.020 |
=0.30 |
=0.08 |
=0.30 |
=0.020 |
=0.30 |
0.040 |
|
P265GH |
1.0425 |
=0.20 |
=0.40 |
=1.40 |
0.025 |
0.020 |
=0.30 |
=0.08 |
=0.30 |
=0.020 |
=0.30 |
0.040 |
|
16Mo3 |
1.5415 |
0.12-0.20 |
0.40-0.90 |
0.40-0.90 |
0.025 |
0.020 |
=0.30 |
0.25-0.35 |
=0.30 |
=0.040 |
=0.30 |
|
|
14MoV6-3 |
1.7715 |
0.10-0.15 |
0.15-0.35 |
0.40-0.70 |
0.025 |
0.020 |
0.30-0.60 |
0.40-0.50 |
=0.30 |
=0.040 |
=0.30 |
|
|
13CrMo4-5 |
1.7335 |
0.10-0.17 |
=0.15 |
0.40-0.70 |
0.025 |
0.020 |
0.70-1.15 |
0.40-0.60 |
=0.30 |
=0.040 |
=0.30 |
|
|
10CrMo9-10 |
1.7380 |
0.08-0.14 |
0.08-0.14 |
0.30-0.70 |
0.025 |
0.020 |
2.00-2.50 |
0.90-1.10 |
=0.30 |
=0.040 |
=0.30 |
|
|
25CrMo4 |
1.7218 |
0.22-0.29 |
0.22-0.29 |
0.60-0.90 |
0.025 |
0.020 |
0.90-1.20 |
0.15-0.30 |
=0.30 |
=0.040 |
=0.30 |
|
|
15NiCuMoNb5-6-4 |
1.6368 |
=0.17 |
=0.17 |
0.80-1.20 |
0.025 |
0.020 |
=0.30 |
0.25-0.50 |
1.00-1.30 |
=0.050 |
0.50-0.80 |
|
|
X10CrMoVNb9-1 |
1.4903 |
0.08-0.12 |
0.08-0.12 |
0.30-0.60 |
0.025 |
0.020 |
8.00-9.50 |
0.85-1.05 |
=0.40 |
=0.040 |
=0.30 |
|
|
a Element som inte ingår i denna tabell får inte avsiktligt läggas till stålet utan köparens samtycke, med undantag för delar som kan läggas till för att avsluta gjutningen. Alla lämpliga åtgärder ska vidtas för att förhindra tillsats av oönskade element från skrot eller andra material som används i ståltillverkningsprocessen |
||||||||||||
|
b Detta krav är inte tillämpligt förutsatt att stålet innehåller en tillräcklig mängd andra kvävebindande element som ska rapporteras. Vid användning av titan ska tillverkaren verifiera att (Al+Ti/2)=0,020 % |
||||||||||||
|
c Alternativ 2: För att underlätta efterföljande formningsoperationer ska en överenskommen maximal kopparhalt som är lägre än vad som anges och en överenskommen specificerad maximal tennhalt gälla |
||||||||||||
|
d Innehållet i dessa element behöver inte rapporteras om de inte avsiktligt har lagts till i rollbesättningen |
||||||||||||
|
e För väggtjocklek=30 mm kan kolhalten ökas med 0,02 % för gjutning och produktanalys |
||||||||||||
|
f Det övre kolvärdet på 0,23 % får inte överskridas för produktanalys |
||||||||||||
EN 10216-2 Mekanisk egendom
|
Stålkvalitet |
Dragegenskaper vid rumstemperatur |
Slagegenskaper ab |
|||||||||||
|
Namn på stål |
Stålnummer |
Övre sträckgräns eller provhållfasthet ReH eller Rp0,2 för väggtjocklek T Min. |
Draghållfasthet Styrka Rm |
Förlängning En min. % a |
Minsta genomsnittliga absorberade energi KV J vid en temperatur på grader |
||||||||
|
T Mindre än eller lika med 16 |
160 |
40 |
60 |
l |
t |
l |
t |
||||||
|
MPa |
MPa |
MPa |
MPa |
MPa |
20 |
0 |
-10 |
20 |
0 |
||||
|
P195GH |
1.0348 |
195 |
320-440 |
27 |
25 |
40 c |
28 d |
27c |
|||||
|
P235GH |
1.0345 |
235 |
225 |
215 |
360-500 |
25 |
23 |
40 c |
28 d |
27c |
|||
|
P265GH |
1.0425 |
265 |
255 |
245 |
410-570 |
23 |
21 |
40 c |
2s d |
27C |
|||
|
16Mo3 |
1.5415 |
280 |
270 |
260 |
450-600 |
22 |
20 |
40 c |
27 c |
||||
|
14MoV6-3 |
1.7715 |
320 |
320 |
310 |
460-610 |
20 |
18 |
40 c f |
27 c |
||||
|
13CrMo4-5 |
1.7335 |
290 |
290 |
280 |
440-590 |
22 |
20 |
40 c |
27 c |
||||
|
10CrMo9-10 |
1.7380 |
280 |
280 |
270 |
480-630 |
22 |
20 |
40 c |
27 c |
||||
|
25CrMo4 |
1.7218 |
345 |
345 |
345 |
540-690 |
18 |
15 |
40 c f |
27 c |
||||
|
15NiCuMoNb5-6-4 |
1.6368 |
440 |
440 |
440 |
440e |
610-780 |
19 |
17 |
40 c f |
27 c |
|||
|
X10CrMoVNb9-1 |
1.4903 |
450 |
450 |
450 |
450 |
630-830 |
19 |
17 |
40 c f |
27 c |
|||
|
a I=längsgående t=tvärgående |
|||||||||||||
|
b Ska verifieras när alternativ 4 och/eller 5 är specificerade, om inte fotnot f) gäller |
|||||||||||||
|
c Alternativ 4: Effektenergi ska verifieras. |
|||||||||||||
|
d Alternativ 5: Longitudinell kollisionsenergi ska verifieras. |
|||||||||||||
|
e För väggtjocklek 60 mm< T =80mm |
|||||||||||||
|
f Slagprov obligatoriskt för väggtjocklek T =16mm |
|||||||||||||
EN 10216-2 pannrör Värmebehandling
|
Stålkvalitet |
Värmebehandling a |
Austeniserande |
Härdning |
|||
|
Namn på stål |
Stålnummer |
Temperaturgrad |
Kylmedium |
Temperaturgrad |
Kylmedium |
|
|
P195GH |
1.0348 |
+N b |
880 till 940 |
Luft |
- |
- |
|
P235GH |
1.0345 |
+N b |
880 till 940 |
Luft |
- |
- |
|
P265GH |
1.0425 |
+N b |
880 till 940 |
Luft |
- |
- |
|
16Mo3 |
1.5415 |
+N b |
890 till 950 |
Luft |
- |
- |
|
14MoV6-3 |
1.7715 |
+NT bc |
930 till 990 |
Luft |
680 till 730 |
luft |
|
13CrMo4-5 |
1.7335 |
+NT bc |
900 till 960 |
Luft |
660 till 730 |
luft |
|
10CrMo9-10 |
1.738 |
+NT bc |
900 till 960 |
Luft |
680 till 750 |
luft |
|
25CrMo4 |
1.7218 |
+QT |
860 till 900 |
Luft eller vätska |
620 till 680 |
luft |
|
15NiCuMoNb5-6-4 |
1.6368 |
+NT c |
880 till 980 |
Luft |
580 till 680 |
luft |
|
X10CrMoVNb9-1 |
1.4903 |
+NT c |
1040 till 1090 |
luft |
730 till 780 |
luft |
|
a +N=Normaliserande, +NT=Normalisering + Temperering, +QT=Släckning + Tempering (luft eller vätska), +I=Isotermisk glödgning. |
||||||
|
b Normalisering inkluderar normalisering av formning. |
||||||
|
c For these steel grades it may be necessary in the case of wall thickness T above 25 mm or T/D >0,15 för att applicera härdning och härdning för att uppnå avsedd struktur och materialegenskaper. Beslutet ska överlåtas till tillverkaren men ska meddelas kunden vid förfrågan och beställning. Stålrör som behandlats på ett sådant sätt ska betecknas med stålnamnet kompletterat med symbolen +QT. |
||||||